Dielectric and relaxation behaviors of (PbMg1/3Nb2/3O3)0.67(PbTiO3)0.33 single crystal
Schmidt, V. Hugo
MetadataShow full item record
Dielectric permittivity along the  direction has been measured as a function of temperature for a relaxor ferroelectric single crystal (PbMg1/3Nb2/3O3)0.67(PbTiO3)0.33 (PMN-33%PT). A sharp ferroelectric phase transition was observed near 425 K and 429 K for cooling and heating processes, respectively. As temperature decreases, a diffuse phase transition (which begins near 330 K upon cooling) was detected. In addition, the nature of the thermal hysteresis for the dielectric permittivity confirms that these transitions (near 330 and 425 K upon cooling) are diffuse first-order and first-order, respectively. The frequency-dependent dielectric data ∊′111 (ƒ, T) prove the existence of an electric dipolar relaxation process between 350 and 400 K. The activation energy, the Vogel-Fulcher temperature and attempt frequency corresponding to this relaxation process are also calculated.
C.-S. Tu, V.H. Schmidt, H. Luo, and F.-C. Chao, “Dielectric and relaxation behaviors of (PbMg1/3Nb2/3O3)0.67(PbTiO3)0.33 single crystal,” Ferroelectrics Letters Section 27, 49-57 (2000).